中文摘要: 半球谐振子的寿命和损伤是直接影响高精度半球谐振陀螺使用时长和安全性的重要因素。目前国内加工的半球谐振子所用的熔融石英玻璃材料主要依靠进口，采用传统的疲劳寿命实验确定方法成本过于昂贵，因此需要利用疲劳分析软件对半球谐振子的疲劳寿命进行分析。文章通过半球谐振陀螺应力分析，采用ANSYS软件对熔融石英半球谐振子进行应力分析仿真，确定因残余应力所引起的疲劳危险部位，并在疲劳部位进行裂纹扩展分析，得到 、 和 型应力强度因子，以使在半球谐振子结构设计和使用过程中对易疲劳的部位进行有效监控和预防。
Abstract:The life and damage of hemispherical resonator are important factors that directly affect the service time and safety of high-precision hemispherical resonator gyro. However, the fused silica glass material used in the hemispherical resonator which processed in China is mainly imported, and it is too expensive to use the traditional fatigue life experiment, so it is necessary to use the software of fatigue life analysis to analyze its fatigue life. In the paper, the ANSYS software is used to analyze the fatigue life of fused silica hemispherical resonator, to determine the dangerous parts caused by the residual stress, to analyze the crack propagation in the fatigue parts, and to obtain the sum stress intensity factor, so as to effectively monitor and prevent the fatigue prone parts in the process of structural design and use of the hemispherical resonator.
keywords: hemispherical resonator gyro (HRG) fatigue life fused silica glass the residual stress stress intensity factor (SIF) the crack propagation
文章编号：20210104 中图分类号：U666.12 文献标志码：A
基金项目:国家重点研发计划项目（2017YFC0704200）；陕西省自然科学基础研究计划项目（2020JM-488）
| 作者 | 单位 |
| 宋丽君 | 西安建筑科技大学信息与控制工程学院 |
| 周 蕾 | 西安建筑科技大学信息与控制工程学院 |
| 段 杰 | 上海航天控制技术研究所 |
| 孙湘钰 | 上海航天控制技术研究所 |
| 李绍良 | 上海航天控制技术研究所 |
| 路明慧 | 西安建筑科技大学信息与控制工程学院 |
引用文本：
宋丽君,周 蕾,段 杰,孙湘钰,李绍良,路明慧.半球谐振子疲劳寿命分析与仿真[J].飞控与探测,2021,(1):36-45.
宋丽君,周 蕾,段 杰,孙湘钰,李绍良,路明慧.半球谐振子疲劳寿命分析与仿真[J].飞控与探测,2021,(1):36-45.